Glazes Yui — Frame

Edit

Solfa

Oxidation

Description / Colour

Yellow lustre and glass super runny, interesting but requires control on application

Finish

Glossy

Texture

Running

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Nepheline Syenite 60% Whiting 20% EPK Kaolin 10% Zinc Oxide 10% Yellow Ochre 5%

Notes

too runny, but colour and pattern are nice

CONNECTIONS

Edit

Solfa 2

Oxidation

Description / Colour

Yellow stone like surface, nice but more variegation to be aimed more drama

Finish

Matte

Texture

PinholeLustre

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Nepheline Syenite 45% EPK Kaolin 20% Whiting 15% zinc oxide 5% yellow ochre 5% Titanium Dioxide 2%

CONNECTIONS

Edit

Buttery Matte White

Oxidation

Description / Colour

White translucent, good starting point

Finish

Semi-matte

Texture

Running

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Potash Feldspar 50% EPK Kaolin 25% Dolomite 20% Borate de calcium 5%

CONNECTIONS

Edit

Sung

Oxidation

Description / Colour

Dark Red something starting but need more test for variegation

Finish

Glossy

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Potash Feldspar 70% Silica 15% Dolomite 10% Red Iron Oxide 5% Rutile 2%

CONNECTIONS

Edit

Buttery Matte White 2

Oxidation

Description / Colour

Cream white

Finish

Semi-matte

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

EPK Kaolin 40% Potash Feldspar 35% Dolomite 20% Borate de calcium 5% Zircopax 5%

Notes

with MRH clay brings bubble? it came bit too opaque, it can be inbetween BMW and BMW2, but nice cream white

CONNECTIONS

Edit

Buttery Matt Jade

Oxidation

Description / Colour

Jade like green with internal flow movement, white background to be tested

Finish

Semi-matte

Texture

Running

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Potash Feldspar 50% EPK Kaolin 25% Dolomite 20% Borate de calcium 5% Tin Oxide 1% Copper Carbonate 0.5%

Notes

Need to check with white slip underneath

CONNECTIONS

Edit

Sung 2

Oxidation

Finish

GlossySatin

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Potash Feldspar 40% Silica 25% Craie 15% EPK Kaolin 12% Dolomite 8% Rutile 3% Red Iron Oxide 2%

CONNECTIONS

Edit

White Matte Slip

Oxidation

Description / Colour

Paper White

Finish

Matte

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

EPK Kaolin 65% Zircopax 20% Potash Feldspar 15%

Notes

Single layer if not pealed

Edit

Black Wash

Oxidation

Description / Colour

Blue Metal Black on red clay

Finish

Semi-matte

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Water 95% Red Iron Oxide 3% Manganese Dioxide 2% Bentonite 1%

Notes

Better on red clay

Edit

Buttery Matte White 2 + mrh slip with 2% SiC

Oxidation

Description / Colour

First lava-ish test, effect is there but under layer needs treatment

Finish

Semi-matte

Texture

Lava

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Notes

Mrh Slip with SiC shrinks badly while drying, it seems the big cause of curling, next try with Black Wash + SiC + gum Arabic without clay as under layer.

CONNECTIONS

Edit

T7G+Titan oxide 10%

Description / Colour

Unexpected Purple Pink, interesting spot effect

Finish

Matte

Notes

Green T7G became Pink with titanium oxide

Edit

Dry Metal Bronze

Oxidation

Description / Colour

Lusty silver to gold movement

Finish

Semi-matte

Texture

Lustre

Fire type

Oxidation

Temperature

1250°C

Clay body

stoneware

Ingredients

Potash Feldspar 65% Manganese Dioxide 25% Red clay 5% Copper Oxide 5%