Glazes Yui — Frame

Edit

Solfa

Oxidation

色

Yellow lustre and glass super runny, interesting but requires control on application

仕上がり

Glossy

質感

Running

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Nepheline Syenite 60% Whiting 20% EPK Kaolin 10% Zinc Oxide 10% Yellow Ochre 5%

メモ

too runny, but colour and pattern are nice

CONNECTIONS

Edit

Solfa 2

Oxidation

色

Yellow stone like surface, nice but more variegation to be aimed more drama

仕上がり

Matte

質感

PinholeLustre

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Nepheline Syenite 45% EPK Kaolin 20% Whiting 15% zinc oxide 5% yellow ochre 5% Titanium Dioxide 2%

CONNECTIONS

Edit

Buttery Matte White

Oxidation

色

White translucent, good starting point

仕上がり

Semi-matte

質感

Running

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Potash Feldspar 50% EPK Kaolin 25% Dolomite 20% Borate de calcium 5%

CONNECTIONS

Edit

Sung

Oxidation

色

Dark Red something starting but need more test for variegation

仕上がり

Glossy

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Potash Feldspar 70% Silica 15% Dolomite 10% Red Iron Oxide 5% Rutile 2%

CONNECTIONS

Edit

Buttery Matte White 2

Oxidation

色

Cream white

仕上がり

Semi-matte

焼成

Oxidation

温度

1250°C

土

stoneware

原料

EPK Kaolin 40% Potash Feldspar 35% Dolomite 20% Borate de calcium 5% Zircopax 5%

メモ

with MRH clay brings bubble? it came bit too opaque, it can be inbetween BMW and BMW2, but nice cream white

CONNECTIONS

Edit

Buttery Matt Jade

Oxidation

色

Jade like green with internal flow movement, white background to be tested

仕上がり

Semi-matte

質感

Running

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Potash Feldspar 50% EPK Kaolin 25% Dolomite 20% Borate de calcium 5% Tin Oxide 1% Copper Carbonate 0.5%

メモ

Need to check with white slip underneath

CONNECTIONS

Edit

Sung 2

Oxidation

仕上がり

GlossySatin

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Potash Feldspar 40% Silica 25% Craie 15% EPK Kaolin 12% Dolomite 8% Rutile 3% Red Iron Oxide 2%

CONNECTIONS

Edit

White Matte Slip

Oxidation

色

Paper White

仕上がり

Matte

焼成

Oxidation

温度

1250°C

土

stoneware

原料

EPK Kaolin 65% Zircopax 20% Potash Feldspar 15%

メモ

Single layer if not pealed

Edit

Black Wash

Oxidation

色

Blue Metal Black on red clay

仕上がり

Semi-matte

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Water 95% Red Iron Oxide 3% Manganese Dioxide 2% Bentonite 1%

メモ

Better on red clay

Edit

Buttery Matte White 2 + mrh slip with 2% SiC

Oxidation

色

First lava-ish test, effect is there but under layer needs treatment

仕上がり

Semi-matte

質感

Lava

焼成

Oxidation

温度

1250°C

土

stoneware

メモ

Mrh Slip with SiC shrinks badly while drying, it seems the big cause of curling, next try with Black Wash + SiC + gum Arabic without clay as under layer.

CONNECTIONS

Edit

T7G+Titan oxide 10%

色

Unexpected Purple Pink, interesting spot effect

仕上がり

Matte

メモ

Green T7G became Pink with titanium oxide

Edit

Dry Metal Bronze

Oxidation

色

Lusty silver to gold movement

仕上がり

Semi-matte

質感

Lustre

焼成

Oxidation

温度

1250°C

土

stoneware

原料

Potash Feldspar 65% Manganese Dioxide 25% Red clay 5% Copper Oxide 5%